C63200 characteristics: good heat workability. C63200 aluminum bronze is mainly used as bar, forgings, bolts, nuts, pump parts, corrosion resistant parts. |
||||||||||||||
|
Name |
Copper or copper alloy UNS number |
Main chemical composition,% |
Copper or copper alloy UNS number |
Name |
Recommended casting temperature |
Forging rating A. |
||||||||
|
Copper |
Lead |
Iron |
Nickel (cobalt) |
Aluminium |
Silicon |
Manganese |
≥ of specified range elements + copper |
°F |
K |
|||||
|
Aluminum nickel Bronze |
C63200 |
Residual residue |
≤0.02 |
E 3.5-4.3 |
4.0-4.8 |
8.7-9.5 |
≤0.10 |
1.2-2.0 |
99.5 |
C63200 |
Aluminum nickel bronze |
1450-1700 |
1060-1200 |
75 |
|
China |
ISO of international standards |
Former Soviet Union |
United States (SYMBOL) |
Japan |
Germany |
Britain |
France |
|
... |
CuAl10Ni |
... |
C63200 |
... |
CW307G |
CA104 |
... |
|
C95500 characteristics: good cutting ability, good mechanical properties, can withstand cold. Hot pressure processing, easy welding, brazing well, good stability to general corrosion, but there is a tendency of corrosion and rupture, mainly used in air conditioning valves, hardware machinery and so on. |
|||||||||||||
|
Name |
Copper alloy UNS number |
Main chemical composition/% |
Category |
Copper alloy UNS number |
Ksi[Mpa] of minimum tensile strength |
Minimum yield strength Ksi[Mpa] |
Extensions from 2 inches [50.08 mm],% |
Bush Hardness (Load 3000- kg) |
|||||
|
Copper |
Aluminium |
Titanium |
Manganese |
Nickel (including cobalt) |
|||||||||
|
Nickel aluminium Bronze |
C95500 |
≥78.0 |
10.0-11.5 |
3.0-5.0 |
≤3.5 |
3.0-5.5 |
Nickel aluminum bronze |
as cast |
C95500 |
90[620] |
40[275] |
6 |
190 |
|
Heat treatment |
|
|
Solution treatment (not less than 1 hour followed by water quenching) |
Annealing (not less than 1 hour after air cooling) |
|
1600-1700°F [870-925℃] |
925-1000°F [495-540℃] |
|
China |
ISO of international standards |
Former Soviet Union |
United States (SYMBOL) |
Japan |
Germany |
Britain |
France |
|
... |
CuAl10Fe5Ni5-C |
C95500 |
CC333G |
AB2-C |
C95520 characteristics: high mechanical properties, good corrosion resistance in atmosphere, fresh water and seawater, good casting performance, compact alloy structure, high air tightness, good wear resistance, can be welded, not easy to braze. C95520 cast copper alloy for corrosion-resistant, wear-resistant parts, simple shape of large castings
|
Name |
Copper alloy UNS number |
Main chemical composition/% |
||||||
|
Copper |
Aluminium |
Titanium |
Manganese |
Nickel (including cobalt) |
Silicon |
Lead |
||
|
Nickel aluminum bronze |
C95520A |
≥74.5 |
10.5-11.5 |
4.0-5.5 |
≤1.5 |
4.2-6.0 |
≤0.15 |
≤0.03 |
|
Heat treatment |
|
|
Solution treatment (not less than 1 hour followed by water quenching) |
Annealing (not less than 1 hour after air cooling) |
|
1600-1700°F [870-925℃] |
925-1000°F [495-540℃] |
C95600 features: with good cutting grinding performance, can be welded, easy to hot machining molding. Aluminum bronze is mainly used to make high strength and wear-resistant structural parts such as support, gear, shaft sleeve, bushing, nozzle, flange, rocker arm, guide valve, pump rod, cam, fixed nut, etc.
|
Name |
Copper alloy UNS number |
Main chemical composition/% |
Copper alloy UNS number |
Ksi[Mpa] of minimum tensile strength |
Minimum yield strength Ksi[Mpa] |
Extensions from 2 inches [50.08 mm],% |
|||
|
Copper |
Aluminium |
Nickel (including cobalt) |
Silicon |
||||||
|
Silicon aluminum bronze |
C95600 |
≥88.0 |
6.0-8.0 |
≤0.25 |
1.8-3.2 |
C95600 |
60[415] |
28[195] |
10 |
C95700 features: high mechanical properties, good wear resistance and corrosion resistance, can be welded, not easy to braze, large castings since 700℃ air cooling can prevent brittle.
|
Name |
Copper alloy UNS number |
Main chemical composition/% |
Copper alloy UNS number |
Ksi[Mpa] of minimum tensile strength |
Minimum yield strength Ksi[Mpa] |
Extensions from 2 inches [50.08 mm],% |
||||||
|
Copper |
Aluminium |
Titanium |
Manganese |
Nickel (including cobalt) |
Silicon |
Lead |
||||||
|
Manganese Nickel Aluminum Bronze |
C95700 |
≥71.0 |
7.0-8.5 |
2.0-4.0 |
11.0-14.0 |
1.5-3.0 |
≤0.10 |
≤0.03 |
C95700 |
90[620] |
40[275] |
20 |
|
China |
ISO of international standards |
Former Soviet Union |
United States (SYMBOL) |
Japan |
Germany |
Britain |
France |
|
ZCuAl8Mn13Fe3Ni2 |
... |
HBBa-70 |
C95700 |
ALBC4 |
Al-MnBZ13 |
CMA1 |
... |
|
C95800 characteristics: aluminum bronze containing iron and manganese elements, belonging to high strength heat resistant bronze, stable mechanical properties at high temperature (400℃), good friction reduction, good corrosion resistance in atmosphere, fresh water and sea water, good pressure processing under hot state, heat treatment strengthening, welding, not easy fiber welding, good cutting performance. |
|||||||||||||
|
Name |
Copper alloy UNS number |
Main chemical composition/% |
Copper alloy UNS number |
Ksi[Mpa] of minimum tensile strength |
Minimum yield strength Ksi[Mpa] |
Extensions from 2 inches [50.08 mm],% |
Bush Hardness (Load 3000- kg) |
||||||
|
Copper |
Aluminium |
Titanium |
Manganese |
Nickel (including cobalt) |
Silicon |
Lead |
|||||||
|
Nickel aluminum bronze |
C95800 |
≥79.0 |
8.5-9.5 |
C 3.5-4.5 |
0.8-1.5 |
4.0-5.0 |
≤0.10 |
≤0.03 |
C95800 |
85[585] |
35[240] |
15 |
... |
|
China |
ISO of international standards |
Former Soviet Union |
United States (SYMBOL) |
Japan |
Germany |
Britain |
France |
|
ZCuAl9Fe4Ni4Mn2 |
... |
BPAЖHMЦ(9-4-4-1) |
C95800 |
ALBC3 |
... |
AB2 |
CuAl10Fe5Ni5 |
|
Name |
Copper alloy UNS number |
Main chemical composition/% |
Category |
Copper alloy UNS number |
Ksi[Mpa] of minimum tensile strength |
Minimum yield strength Ksi[Mpa] |
Extensions from 2 inches [50.08 mm],% |
||||||
|
Copper |
Aluminium |
Titanium |
Manganese |
Nickel (including cobalt) |
Silicon |
||||||||
|
C95820B |
≥77.5 |
9.0-10.0 |
4.0-5.0 |
≤1.5 |
4.5-5.8 |
≤0.10 |
≤0.02 |
Nickel aluminum bronze |
as cast |
C95820 |
94[650] |
39[270] |
13 |